TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity, HAAKE RV-20 Rotoviscometer, mPa·s (cP):
Cone 1o @ Shear rate 22 s
-1 9,000
Work Life @ 25°C, hours 8 to 16
Shelf Life @ -40°C (from date of manufacture), days 365
TYPICAL CURING PERFORMANCE
Cure Schedule
30 minutes @ 150°C
Suggested temperature cures are from 150 to 350oC. For
applications requiring higher electrical conductivity, a cure cycle of 15
minutes @ 300oC is recommended. Product properties will not be
reduced by subsequent post die attach thermal exposure, i.e.,
wirebond, and/or lid seal up to 370oC.

TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Coefficient of Thermal Expansion, :
Below Tg, ppm/°C 33
Glass Transition Temperature (Tg) by TMA, °C 240
Bulk Thermal Conductivity, W/(m-K):
@ 90°C 1.1
@ 165°C 1.0
Tensile Modulus, DMTA :
Cured 30 minutes @ 300oC N/mm2 10,000
(psi) (1,450,377)
Extractable Ionic Content, @ 100°C:
Chloride (Cl-) <10
Sodium (Na+) <15
Potassium (K+) <15
Decomposition (in N2):
TGA analysis @ 10oC/ minute ramp from 25 to 400
oC
@ 340oC, % 0.2
@ 400oC, % 0.3
Electrical Properties
Sample cured 30 minutes @ 300oC
Volume Resistivity, ohm-cm ≤0.01

TYPICAL PERFORMANCE OF CURED MATERIAL
Die Shear Strength:
2 X 2 mm Si die, kg-f,
cured 20 minutes @ 150oC
Substrate DSS
Ag/Cu LF ≥5
Tensile Strength :
cured 30 minutes @ 300oC, MPa
After Cure After 1000 TC'C"
>17 >17
Radius of Curvature:
Si die on Alumina, meters
cured 30 minutes @ 300oC
Chip Size: ROC
15 x 15 mm > 5

• 

  漢高樂泰導電膠,楊浦厚膜漢高ABLESTIKJM7000導電膠

  面議

  產品名：漢高ABLESTIKJM7000導電膠,JM7000導電膠,漢高導電膠,樂泰導電膠

• 

  ablestik84-1A導電膠

  面議

  產品名：導電膠,耐高溫導電膠,84-1A導電膠,84-1LMI導電膠

• 

  平涼樂泰648固持膠固化劑

  面議

  產品名：樂泰648固持膠,固化劑

• 

  臺東縣樂泰EA-E20HP樹脂膠樂泰EA-E20HP樹脂膠

  面議

  產品名：樂泰EA-E20HP 樹脂膠,樂泰EA-E20HP樹脂膠

• 

  新鄉樂泰EA3463環氧修補劑環氧修補劑

  面議

  產品名：樂泰EA 3463環氧修補劑,環氧修補劑

• 

  天水樂泰環氧灌封膠FP4531

  面議

  產品名：樂泰環氧灌封膠,FP4531,底部填充劑

• 

  酉陽樂泰542螺紋膠

  面議

  產品名：樂泰542 螺紋膠,螺紋密封膠

• 

  黑河樂泰SF7070清洗劑

  面議

  產品名：樂泰 SF 7070 清洗劑,噴罐清洗劑